Title

Magnetic phase diagram of the ferromagnetic compound CeAgSb₂ under high pressure

Abstract

In heavy fermion compounds, even if the material has a magnetic ground state, the magnetic ordering temperature may be suppressed by applying pressure. And after being completely suppressed, in some case, superconductivity appears.
I will present the paper about heavy fermion compound, CeAgSb₂. Electrical resistivity and ac-calorimetric measurements reveal a complex magnetic phase diagram at high pressures up to 80 kbar for single crystals of the ferromagnetic compound CeAgSb₂. The ferromagnetic order at T_C = 9.6 K at ambient pressure is completely suppressed at P_c ∼ 35 kbar (T_C = 0 K). Another magnetic transition, possibly antiferromagnetic, found above 27 kbar, attains a maximum value T_N = 6 K at 44 kbar and then appears to be completely suppressed by pressure of around 50 kbar. At ambient pressure, no superconductivity was observed above 0.1 K, and under pressure in the ferromagnetic state (P = 28.5 kbar) nor in the antiferromagnetic state (P = 33-46 kbar) no superconductivity above 0.3 K.

概要

重い電子系化合物において、物質が基底状態で磁気的な秩序を持つ場合でも、その磁性秩序を形成する温度は、加圧に伴い徐々に抑圧され低くなっていくことがあり、そして完全にその温度が消失した先に、超伝導が観測されることもある。 本発表では、重い電子系化合物CeAgSb₂についての論文を紹介する。強磁性体であるCeAgSb₂の単結晶に対して、常圧から80 kbarまでの圧力域で、電気抵抗と熱量の測定を行ったところ、複雑な磁気相図が得られた。CeAgSb₂の常圧下での強磁性転移温度（T_C）は9.6 Kであるが、加圧することにより、約35 kbarで完全に強磁性は消失した（すなわちT_C = 0 Kとなる）。27 kbar以上では、反強磁性転移とみられるもう一つ別の磁気転移が観測された。転移温度（T_N）は44 kbarにおいて最大値6 Kをとり、その後約50 kbarで完全に消失した。しかし、常圧下で0.1 Kまで温度をさげても超伝導は観測されず、圧力下においても、強磁性状態（P = 28.5 kbar）、反強磁性状態（P = 33-46 kbar）のいずれの場合も0.3 K以上で超伝導は発現しなかった。