Some Ce-compounds have the magnetic order in ground state. Most of them show antiferromagnetic ordering while only few compounds order ferromagnetically.

I'll introduce the result of study of the ferromagnet, CeRhSn₂.

The abstract of the paper is as follows. The measurements of magnetization, electrical resistivity and magnetoresistance on CeRhSn₂ carried out. In the resistivity and magnetization measurement, the phase transition seems to be ferromagnetic one was observed at ∼4.0 K. The resistivity was similar to that of other Ce-compounds which order magnetically. The magnetoresistance was generally negative and the value of the resistivity at 2 K and 10 T decreased by 41% comparing with that at 0 T. This behavior shows the ferromagnetic one but indicated the complicated magnetic phase diagram too.

The last time, I talked to the pressure-induced ferro-antiferromagnetic transition of CeAgSb₂. Now I am carrying out the study of CePd2Ga₃ in which the similar phase transition is suggested. I'll also introduce my study.

Ce系化合物には基底状態で磁気秩序を持つものが多くあるが、そのほとんどが反強磁性体であり、強磁性を示すものはまれである。

本発表では、強磁性体であるCeRhSn₂についての研究結果を紹介する。

以下に、論文の概要を記す。CeRhSn₂において、磁化、電気抵抗、磁気抵抗の測定結果を行った。電気抵抗測定と磁化測定により、約4.0 Kで強磁性転移と思われる相転移が観測され、電気抵抗率は、他の磁気秩序を持つCe系化合物のものと同様のふるまいを示した。磁気抵抗効果は、全体的に負であり、2 Kおよび10 Tにおける電気抵抗率は、0 Tの時より約41%減少した。これは強磁性的なふるまいではあるが、複雑な磁気相図を反映する結果も得られた。

前回は、CeAgSb₂における圧力誘起強磁性-反強磁性転移について発表したが、現在、私は同様の相転移が示唆されているCePd2Ga₃について研究を進めており、この論文からの考察も交えて発表する。

Z. Hossain et al., J. Phys.: Condens. Matter. 14 (2002) 9687-9691