Iodanil (C6O2I4) is known as a single-component molecular crystal showing a pressure-induced metallization above 33 GPa and a superconducting transition at 2K at 52 GPa. Then, the molecularity of iodanil in the high-pressure metallic phase was confirmed by IR absorption measurement. In order to clarify the pressure-induced metallization mechanism, powder x-ray diffraction measurements on iodanil have been carried out at pressures up to 39 GPa at room temperature with a diamond-anvil cell under the best hydrostatic conditions using helium as the pressure-transmitting medium. The diffraction patterns up to 23.3 GPa were fitted with a space group P21/c. New peaks appeared above 26.8 GPa and their intensities increased with increasing pressure while the original ones observed for the low-pressure phase were gradually depressed. This phase transition was accompanied with a mixed state of low- and high-pressure phases over the wide pressure range between 26.8 and at least 39 GPa.
ヨーダニルは33GPa以上で圧力誘起金属化し、52GPa、2Kで超伝導転移する単一成分の分子性結晶として知られている。また、IR測定により、高圧の金属相において、分子性を維持していることがわかった。 ヨーダニルの圧力誘起金属化のメカニズムを明らかにするために、ダイアモンドアンビルセル(DAC)を用いたヨーダニルの粉末X線回折測定が室温の下、39GPaまでの圧力範囲で行われた。圧力媒体として、静水圧性が一番高いと言われているヘリウムを使用した。23GPaまでの回折パターンは空間群P21/cでフィッティングされた。26.8GPa以上で新しいピークが現れ、圧力を増すと、その強度は増加した。一方、低圧相で観測された元のピークは次第に弱くなっていった。この相転移は、低圧相と高圧相が混合していることに起因しており、それは26.8GPaから少なくとも39GPaと広い圧力領域において起こっている。