Possible formation of oxides or thin oxide films on late transition metals has been recently recognized as an essential ingredient to understand catalytic oxidation reactions under technologically relevant gas phase conditions. Among these metals, Pd is unique in various aspects. It forms a surface oxide structure which is the so-called root 5 structure. This structure is observed in UHV conditions. CO oxidation on Pd(100) has been focused on as an example of catalytic reactions on Pd. The stability of Pd surface structures [1] and reaction paths of CO oxidation[2] are calculated theretically. These results imply that the root 5 structure is stable in catalytically relevant conditions. The authors of these theoretical works imply that the root 5 structure is relevant for the CO oxidation.
後周期遷移金属上の酸化物や酸化膜の形成は、技術的に関連のある気相環境下での酸化反応を理解するうえで、重要な材料であると認識されている。こういった金属のなかで、Pdは超高真空化ではルート5構造と呼ばれる酸化膜を形成することが知られている。Pd表面上の一酸化炭素の酸化反応に着目し、Pd表面構造の安定性と一酸化炭素の反応経路について、理論計算が行われた。これらの結果は、触媒動作に関連のある環境下で、ルート5構造が安定であり、ルート5構造上で一酸化炭素の酸化が関係していることを示唆している。