Ba1-xKxBiO3 system has been extensively studied as superconductor. The electrical conductivity depnds on its potassium doping ratio. High potassium content one (x > 0.35) is metallic, on the other hand, low potassium content one (x < 0.35) is semiconducting. Metallic Ba1-xKxBiO3 shows superconducting transition and the transition temperature Tc depends on potassium doping ratio, too. Low potassium content one (x < 0.35) is expected to have semiconductor-metal transition and superconducting transition (with higher Tc) under high pressure. Therefore, this presentation shows some high pressure electrical resistance measurements about Ba1-xKxBiO3 with x = 0.4, 0.3, 0.15, 0. About x = 0.4, Tc increases with applying pressure up to 1 GPa. About x = 0.3, the result implies that it can have semiconductor-metal transition (and higher Tc) under higher pressure (P >> 1 GPa). About x = 0.15 and 0, pressure-induced semiconductor-metal transition doesn't occur up to 8 GPa. To clarlfy pressure effect in this system, higher pressure studies are demanded.
Ba1-xKxBiO3系は超伝導体として盛んに研究されてきた。その電気伝導性はカリウム濃度に依存し、カリウム濃度が高いもの（x > 0.35）は金属的、カリウム濃度が低いもの（x < 0.35）は半導体的になっている。金属のBa1-xKxBiO3は超伝導転移を示し、その転移温度Tcもまたカリウムドープ量に依存している。圧力下ではカリウムドープ量の少ないものが半導体金属相転移を起こし、（より高いTcの）超伝導転移を起こすことが期待されている。そこでこの発表では、x = 0.4, 0.3, 0.15, 0のBa1-xKxBiO3についての高圧力下での電気抵抗測定を紹介する。x = 0.4のものについては、1 GPa以下では加圧に対してTcは増加するという結果が得られた。x = 0.3のものについては、より高い圧力下（P >> 1 GPa）で半導体金属相転移（とより高い温度での超伝導転移）が起こる可能性を示唆する結果が得られた。x = 0.15, 0のものについては、8 GPa以下では半導体金属相転移は起こらなかった。この系での圧力効果を明確にするためには、さらに高圧力下での実験が必要である。