More than 20 years ago, various cuprate superconductors has been discovered, which had superconducting transition temperature (T_c) higherthan 30 K. Although the mechanism still has many mysteries, applying pressure is able to change T_c and a lot of researches with pressure have been studied. Hg cuprate system recorded the highest T_c (=164 K) under high pressure (31 GPa) in 1994 [1]. To make new world record of the highest T_c under the pressure with HgBa₂Ca₂Cu₃O_8+δ (Hg-1223), we found that it needs the best condition of the pressure, purity of the sample, amount of the doping carriers and so on.

In this presentation, I would like to introduce you about my research. In this work, high purity Hg-1223 samples synthesized were used. We measured electrical resistance for these samples under the hydrostatic pressure or non-hydrostatic pressure with a diamond-anvil cell (DAC).

銅酸化物高温超伝導体が発見されてから20年以上が経ったが、高い温度で超伝導が発現する機構は完全には解明されておらず、まだ多くの謎が残されている。圧力を加えると超伝導転移温度(T_c)が変化することから、圧力を用いた数多くの実験が行われてきた。その中でも、Hg系の銅酸化物高温超伝導体において、約31 GPaの圧力下で164 KというT_cの世界記録がマークされた。T_cの世界記録を更新するためには、圧力のコンディションや試料の純良性、キャリアのドープ量など、様々な要素について考慮する必要がある。

今回の発表では、純良性の良いHg-1223の試料を作製し、ダイヤモンドアンビルセルを用いて、静水圧性の高い、あるいは低い条件下で、試料の電気抵抗の温度依存性を測定を行った私の研究について紹介したい。

• L. Gao et al., Phys. Rev. B 50, 4260 (1994)