A sheet shape polymer with monolayer thickness in which all building blocks are linked by covalent bondings in a periodic manner is called two-dimensional (2D) polymer. For the synthesis of the 2D polymer, a following method is generally employed. First monomers are ordered two-dimensionally using self-assembly on substrates or at interfaces. Subsequently, the ordered monomers are linked by covalent bindings through a chemical reaction. The aim of my research project is to synthesize new porous 2D polymers from the monomers ordered at the solid/liquid interfaces. For this purpose, a dehydrobenzo[12]annulene (DBA) derivative having six alkoxy chains, which is known to form a porous honeycomb structure at the solid/liquid interfaces, was chosen as a molecular building block. Moreover a reactive diacetylene unit is introduced to each alkoxy chain for the cross-linking reaction. In this presentation, I will introduce 2D polymers, self-assemblies of organic molecules on surfaces, and a light induced topochemical polymerization of diacetyene group. Finally I will introduce my work.
全ての構成要素が周期的に共有結合で結ばれた単分子膜厚のシート状ポリマーは二次元ポリマーと呼ばれる。この二次元ポリマーの合成には、基板や界面に自己集合によってモノマーを二次元的に配列させた後に、それらを共有結合形成反応により連結する方法が用いられる。私は、固液界面で配列させたモノマーから新奇な多孔性の二次元ポリマーを合成することを目的とした研究を行っている。そのため、固液界面で多孔性のハニカム構造を形成するデヒドロベンゾ[12]アヌレン誘導体に、反応性部位としてジアセチレン部位を導入したモノマー分子を設計し、その合成に取り組んでる。本発表では二次元ポリマー、固体表面での自己集合およびジアセチレンの光橋架け反応を紹介し、最後に私の研究テーマについて述べる。