A sheet shape polymer with monolayer thickness in which all building blocks are linked by covalent bondings in a periodic manner is called two-dimensional (2D) polymer. The synthesis of the 2D polymer and investigation of its properties have been paid great attentions. From my lab., dehydrobenzo[12]annulenes (DBAs) having six linear alkyl chains were reported to form porous honeycomb structures at the solid/liquid interfaces. On the basis of this result, I designed and synthesized a DBA derivative which has a reactive diacetylene unit at the middle of each alkyl chain for the synthesis of a novel porous 2D polymer. Moreover, scanning tunneling observation at the solid/liquid interfaces revealed that this molecule formed a porous honeycomb structure. In this presentation, I will introduce 2D polymers and previous work performed in my laboratory. Finally I talk about my work.
全ての構成要素が周期的に共有結合で結ばれた単分子膜厚のシート状ポリマーは二次元ポリマーと呼ばれ、その合成と物性調査に多大な関心が集まっている。当研究室では以前に六本の直鎖アルキル基を有するデヒドロベンゾ[12]アヌレン (DBA) が固液界面において多孔性のハニカム構造を形成することを報告している。私は多孔性の二次元ポリマーを合成するため、DBA誘導体のアルキル鎖に反応性のジアセチレンを導入した分子を設計し、合成した。さらに、合成した分子が固液界面でハニカム構造を形成することを走査型トンネル顕微鏡観察により明らかにした。本発表では二次元ポリマーについて紹介し、本研究室で行われた先行研究について述べた後、私の研究について説明する。